Explosion-proof Fast-drying Castables

	Refractory products for Blast Furnace
	Refractory products for Mixer
	Refractory products for Converter
	Refractory products for EAF
	Refractory products for Ladle
	Refractory products for Tundish
	Refractory products for Aluminum Electrolysis Cell
	Refractory Products for Industrial Furnaces
	Precast Burner Shapes and Regenerative Case
	Anchor Brick
	High Strength Light-weight Castables
	Light-weight Fiber Castables
	Gunning Mixes
	Plastic Castables
	Clay-based and High-alumina Plastic Castables
	Low-cement, Ultra low-cement and No-cement Castables
	Explosion-proof Fast-drying Castables
	Baking-free high-strength Self-flow Castables
	Self-flow Castables
	Explosion-proof Fast-drying Self-flow Castables
	Baking-free Self-flow Castables
	Abrasive Cr2O3-corundum-based and ZrO2-corundum-based Skid Rail and Block
	High Temperature Barrier
	Ball Regenerator
	Cast Regenerator
	Ceramic Honeycomb Regenerator

NEWS

CONTACTS

Send a message

	name
	tel.
	e-mail

type this nubmer.

PRODUCTS / Refractory Products for Industrial Furnaces /

Explosion-proof Fast-drying Castables

Brand: PN-SP

To shorten baking time of industrial furnaces, explosion-proof fast drying castables are developed by PRCO. Comparing with conventional castables, the baking time may be reduced from around 10 days to 3-5 days, so downtime and cost is dramatically saved.

The PN-SP fast drying castables are titled high-tech products which have been listed in National Level Torch Project and several other prizes such as Provincial Level Science & Technology Advancement. They are ideal solution for installation and maintenance of various industrial furnaces.

Main Properties:

Brand		PN-SP50	PN-SP55	PN-SP60	PN-SP65	PN-SP70	PN-SP9
Al₂O₃(%)≥		50	55	60	65	68	-
Al₂O₃+MgO (%)≥		-	-	-	-	-	75
Bulk density (g/cm³);≥	110℃×16h	2.20	2.25	2.35	2.40	2.45	2.70
Bulk density (g/cm³);≥	1350℃×3h	2.15	2.20	2.30	2.35	2.40	2.65
Cold crushing strength (MPa);≥	110℃×16h	30	45	50	55	60	40
Cold crushing strength (MPa);≥	1350℃×3h	50	60	70	75	80	60
Modulus of rupture (MPa);≥	110℃×16h	5	6	7	8	8	8
Modulus of rupture (MPa);≥	1350℃×3h	8	8	9	10	10	6
Reheat linear change (%)	110℃×16h	0~-0.2	0~-0.2	0~-0.2	0~-0.2	0~-0.2	-
Reheat linear change (%)	1300℃×3h	0~-0.5	0~-0.5	0~-0.5	0~-0.5	0~-0.5	-
Water addition (%)		6.8	6.5	6.0	5.5	5.2	4.8
Normal service temp. (^oC)		1350	1350	1350	1350	1350	1350
Max service temp. (^oC)		1600	1600	1600	1600	1600	1600
Application		Roof and wall					Slag area